| Deposit Hardness | 55-65 HRC |
|---|---|
| Classification | Ni Core, Tungsten Carbide |
| Purpose | Wear Resistance,Anti-Corrosion |
| Carbide Hardness | Minimum 2000 HV0.1 |
| Process | Oxy-acetylene Welding |
| Manufacture | Filled Tubular Rod |
|---|---|
| Chemistry | WFeC |
| Purpose | Wear Resistance |
| Process | Oxy-acetylene Welding |
| Specification | ,Φ4.0*600mm,Φ5.0*600mm,Φ6.0*600mm,Φ7.0*600mm |
| Carbide Hardness | 2100±100HV0.1 |
|---|---|
| Coating Hardness | 55-65HRC |
| Purpose | Wear Resistance |
| Process | Oxy-acetylene Welding |
| Overlay Thickness | 2-8mm |
| Manufacture | Filled Tubular Rod |
|---|---|
| Chemistry | WFeC |
| Purpose | Wear Resistance |
| Process | Oxy-acetylene Welding |
| Specification | ,Φ4.0*600mm,Φ5.0*600mm,Φ6.0*600mm,Φ7.0*600mm |
| Manufacture | Filled Tubular Rod |
|---|---|
| Chemistry | WFeC |
| Purpose | Wear Resistance |
| Process | Oxy-acetylene Welding |
| Specification | ,Φ4.0*600mm,Φ5.0*600mm,Φ6.0*600mm,Φ7.0*600mm |
| Manufacture | Filled Tubular Rod |
|---|---|
| Chemistry | WFeC |
| Purpose | Wear Resistance |
| Process | Oxy-acetylene Welding |
| Specification | ,Φ4.0*600mm,Φ5.0*600mm,Φ6.0*600mm,Φ7.0*600mm |
| Carbide Hardness | 2100±100HV0.1 |
|---|---|
| Coating Hardness | 55-65HRC |
| Purpose | Wear Resistance |
| Process | Oxy-acetylene Welding |
| Name | Flexible Welding Rope |
| Carbide Hardness | 2700±100 HV0.1 |
|---|---|
| Coating Hardness | 55-65HRC |
| Purpose | Wear Resistance |
| Process | Oxy-acetylene Welding |
| Packaging Details | 5kg/10kg/15kg per Coil |
| Carbide Hardness | 2700±100HV0.1 |
|---|---|
| Coating Hardness | 55-65HRC |
| Purpose | Wear Resistance |
| Process | Oxy-acetylene Welding |
| Melting | 950 - 1050°C |
| Materials | WC Particles + Ni/Ag(Cu) Alloy |
|---|---|
| Particle | Dia:1.6-9.5mm |
| Application | Two Types For Various Applications |
| Two Types | Cutting Grades And Wear Grades |
| Rod Length | 450mm |